Low stress asymmetric dual side module

ABSTRACT

Implementations of semiconductor packages may include: a first substrate having two or more die coupled to a first side, a clip coupled to each of the two or more die on the first substrate and a second substrate having two or more die coupled to a first side of the second substrate. A clip may be coupled to each of the two or more die on the second substrate. The package may include two or more spacers coupled to the first side of the first substrate and a lead frame between the first substrate and the second substrate and a molding compound. A second side of each of the first substrate and the second substrate may be exposed through the molding compound. A perimeter of the first substrate and a perimeter of the second substrate may not fully overlap when coupled through the two or more spacers.

CROSS REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of the filing date of U.S.Provisional Patent Application 62/882,119, entitled “LOW STRESSASYMMETRIC DUAL SIDE MODULE” to Chew et al., which was filed on Aug. 2,2019, the disclosure of which is hereby incorporated entirely herein byreference.

BACKGROUND 1. Technical Field

Aspects of this document relate generally to modular semiconductorpackages, such as power semiconductor packages having dual side coolingcapabilities. More specific implementations involve lead frames.

2. Background

Power semiconductor packages generally include multiple stackedsubstrates.

Heat sinks may be coupled to an external terminal of the device. Somepower semiconductor packages may include a heat sink with a fin-arraystructure.

SUMMARY

Implementations of semiconductor packages may include: a first substratehaving two or more die coupled to a first side of the first substrate. Aclip may be coupled to each of the two or more die on the firstsubstrate. The package may also include a second substrate having two ormore die coupled to a first side of the second substrate. A clip may becoupled to each of the two or more die on the second substrate. Thepackage may include two or more spacers coupled to the first side of thefirst substrate. The package may also include a lead frame between thefirst substrate and the second substrate and a molding compoundencapsulating the lead frame. A second side of each of the firstsubstrate and the second substrate may be exposed through the moldingcompound. A perimeter of the first substrate and a perimeter of thesecond substrate may not fully overlap when coupled through the two ormore spacers.

Implementations of semiconductor packages may include one, all, or anyof the following:

The two or more die may include an insulated-gate bipolar transistors(IGBT) die and a fast recovery die (FRD).

The first substrate and the second substrate may include a direct bondedcopper substrate (DBC) with an alumina (Al₂O₃) ceramic doped withzirconium dioxide (ZrO₂), a silicon nitride (Si3N4) ceramic, an aluminumnitride (AlN) ceramic, a high strength AlN (H—AlN) ceramic, or anycombination thereof.

The semiconductor package may also include a heat sink coupled with thesecond side of the first die, the second side of the second die, or anycombination thereof.

The two or more spacers may be made of electrically conductive materialand may electrically couple the first substrate to the second substrate.

The first substrate and the second substrate may include a direct bondedcopper substrate (DBC), an insulated metal substrate technology (IMST)substrate, an active metal bonding (AMB) substrate, or any combinationthereof.

Implementations of semiconductor packages may include: a lead frame anda first substrate mechanically and electrically coupled to a first sideof the lead frame. The first substrate may include two or more die onthe first side of the first substrate. A clip may be coupled to each ofthe two or more die coupled to the first side of the first substrate.The package may also include a second substrate mechanically andelectrically coupled to a second side of the lead frame. The secondsubstrate may include two or more die on the first side of the secondsubstrate and a clip is coupled to each of the two or more die. Thepackage may also include two or more spacers coupled to the first sideof each of the first substrate and the second substrate. A moldingcompound may encapsulate the first side and the second side of the leadframe. The first side of the first substrate and the first side of thesecond substrate may be asymmetrically coupled through the two or morespacers.

Implementations of semiconductor packages may include one, all, or anyof the following:

The two or more die may include an insulated-gate bipolar transistors(IGBT) die and a fast recovery die (FRD).

The first substrate and the second substrate may include a direct bondedcopper substrate (DBC) with an alumina (Al₂O₃) ceramic doped withzirconium dioxide (ZrO₂) a silicon nitride (Si3N4) ceramic, an aluminumnitride (AlN) ceramic, a high strength AlN (H—AlN) ceramic, or anycombination thereof.

The package may also include a heat sink coupled with one of the secondside of the first die, the second side of the second die, or anycombination thereof.

The two or more spacers may be made of electrically conductive materialand electrically couple the first substrate to the second substrate.

The first substrate and the second substrate may include a direct bondedcopper substrate (DBC), an insulated metal substrate technology (IMST)substrate, an active metal bonding (AMB) substrate, or any combinationthereof.

Implementations of semiconductor packages may be manufactured throughmethods of forming semiconductor packages. Various methodimplementations may include: providing a first panel of first substratesand a second panel of second substrates. The method may also includeprinting a first electrically conductive bonding material on the firstside of the first panel of substrates and the second side of the firstpanel of substrates in predetermined locations and coupling two or moredie to each substrate of the first panel of substrates and to eachsubstrate of the second panel of substrates at the predeterminedlocations. The method may also include dispensing a second electricallyconductive material onto a second side of each of the two or more dieand coupling a clip to each of the two or more die. The method mayinclude singulating each of the first panel and the second panel into aplurality of first substrates and a plurality of second substrates,respectively. The method may include dispensing solder onto a pluralityof predetermined locations on the first side of each of the plurality offirst substrates and each of the plurality of second substrates. Themethod may also include coupling a first substrate of the plurality offirst substrates to a first side of a lead frame and coupling two ormore spacers to a first side of the first substrate. The method may alsoinclude coupling a first side of a second substrate of the plurality ofsecond substrates to the two or more spacers and to the second side ofthe lead frame.

Implementations of methods of forming semiconductor packages may includeone, all, or any of the following:

The method may further include trimming the lead frame to expose aplurality of leads and forming the leads.

The method may further include encapsulating the lead frame on the firstside and the second side, wherein a second side of each substrate of theplurality of first substrates and the plurality of second substrates isexposed.

The first panel of first substrates and the second pane of secondsubstrates may each include a direct bonded copper substrate (DBC), aninsulated metal substrate technology (IMST) substrate, an active metalbonding (AMB) substrate, or any combination thereof.

The method may further include coupling a heat sink with one of thesecond side of the first die, the second side of the second die, or anycombination thereof.

The method may further include coupling a heat sink with the second sideof the first substrate of the plurality of first substrates, the secondside of the second substrate of the plurality of second substrates, orany combination thereof.

The two or more spacers may be made of electrically conductive materialand may electrically couple the first substrate to the second substrate.

The first side of the first substrate and the first side of the secondsubstrate may be asymmetrically coupled through the two or more spacers.

The first electrically conductive material and the second electricallyconductive material may include a solder paste or a sintering paste.

The foregoing and other aspects, features, and advantages will beapparent to those artisans of ordinary skill in the art from theDESCRIPTION and DRAWINGS, and from the CLAIMS.

BRIEF DESCRIPTION OF THE DRAWINGS

Implementations will hereinafter be described in conjunction with theappended drawings, where like designations denote like elements, and:

FIG. 1 is a side view of an implementation of a semiconductor package;

FIG. 2 is a top perspective view of an implementation of a semiconductorpackage;

FIG. 3 is a top perspective view of an implementation of a lead framebefore coupling of a second substrate thereto;

FIG. 4 is a top perspective view of an implementation of a firstsubstrate;

FIG. 5 is a top perspective view of an implementation of a secondsubstrate;

FIG. 6 is a top perspective view of an implementation of a panel ofsubstrates;

FIG. 7 is a top perspective view of an implementation of a panel ofsubstrates having electrically conductive material coupled inpredetermined locations;

FIG. 8 is a top perspective view of an implementation of a panel ofsubstrates having two die coupled to predetermined locations;

FIG. 9 is a top perspective view of an implementation of electricallyconductive material coupled to each of the two die;

FIG. 10 is a top perspective view of an implementation of two clipscoupled to each of the two die;

FIG. 11 is a top perspective view of an implementation of a clip;

FIG. 12 is a top perspective view of an implementation of wire bondscoupled to the two die;

FIG. 13 is a top perspective view of an implementation of a panel ofsubstrates with three substrates singulated therefrom;

FIG. 14 is a top perspective view of an implementation of a firstsubstrate after singulation;

FIG. 15 is a top perspective view of an implementation of a secondsubstrate after singulation;

FIG. 16 is a top perspective view of an implementation of a firstsubstrate coupled to a lead frame and a second substrate before couplingto the lead frame;

FIG. 17 is a close up view of an implementation of a spacer;

FIG. 18 is a top perspective view of an implementation of a second sideof a lead frame after coupling of a second substrate thereto;

FIG. 19 is a top perspective view of an implementation of a first sideof a lead frame;

FIG. 20 is a side view of an implementation of a semiconductor package;

FIG. 21 is a top view of an implementation of a semiconductor packageafter encapsulation; and

FIG. 22 is a perspective view of an implementation of a semiconductorpackage after lead trimming and formation.

DESCRIPTION

This disclosure, its aspects and implementations, are not limited to thespecific components, assembly procedures or method elements disclosedherein. Many additional components, assembly procedures and/or methodelements known in the art consistent with the intended semiconductorpackage will become apparent for use with particular implementationsfrom this disclosure. Accordingly, for example, although particularimplementations are disclosed, such implementations and implementingcomponents may comprise any shape, size, style, type, model, version,measurement, concentration, material, quantity, method element, step,and/or the like as is known in the art for such semiconductor packages,and implementing components and methods, consistent with the intendedoperation and methods.

Referring to FIG. 1, a side view of an implementation of a semiconductorpackage 2 is illustrated. As illustrated, the semiconductor packageincludes a first substrate 4 coupled to a first side 6 of a lead frame8. The first substrate 4 includes two die 10 and 12 coupled to the firstsubstrate 4 in two predetermined locations. In various implementations,more than two die may be coupled to the first substrate. By non-limitingexample, the die may include an insulated-gate bipolar transistor(IGBT), a fast recovery die (FRD), any other semiconductor die, or anycombination thereof. The semiconductor package also includes a secondsubstrate 14 coupled to a second side 16 of the lead frame 8. The leadframe 8 is coupled between the first substrate 4 and the secondsubstrate 14. The second substrate has two die coupled to twopredetermined locations on a first side of the second substrate. Invarious implementations, the two die coupled to the second substrate mayinclude, by non-limiting example, an insulated-gate bipolar transistors(IGBT), a fast recovery die (FRD), any other semiconductor die, or anycombination thereof.

Each of the first substrate and the second substrate illustrated in FIG.1 is a direct bonded copper substrate (DBC) including a ceramicsubstrate with a copper plate coupled to a first side and a second sideof the ceramic substrate. In various implementations, the DBC mayinclude an alumina (Al₂O₃) ceramic doped with zirconium dioxide (ZrO₂)(HPS). In other implementations, the ceramic may be made of othermaterials such as a silicon nitride (Si3N4) ceramic, an aluminum nitride(AlN) ceramic, a high strength AlN (H—AlN) ceramic, or any combinationthereof. In some implementations, a thickness of the layers of theCu/HPS/Cu DBC substrate may include 0.30 mm Cu, 0.32 mm ceramic/HPS, and0.30 mm Cu. In other implementations, the thickness may be changed basedon electrical needs, thermal needs, package height control, and otherparameters of the device. In other implementations, either the firstsubstrate, the second substrate, or both the first substrate and thesecond substrate may be made of another substrate material, such as, bynon-limiting example, an active metal brazed (AMB) substrate, aninsulated metal substrate technology (IMST), a laminated substrate, asubstrate with a metal layer on only one surface of the substrate, anycombination thereof, and any other substrate type.

Referring to FIG. 2, a top view of an implementation of a semiconductorpackage 22 is illustrated. In this view, a second side 24 of the leadframe is illustrated having a second substrate 28 coupled thereto. Thesecond substrate 28 may be coupled to the lead frame 24 through leads 30formed in an up position. As illustrated, a first substrate 32 iscoupled to a first side of the lead frame opposite the second substrate.A portion of the first side of the first substrate is facing a portion,but not all of the first side of the second substrate. Also, asillustrated, a perimeter of the first substrate and a perimeter of asecond substrate do not fully overlap when coupled to the lead frame andspacers. The first substrate and the second substrate are accordinglyasymmetrically coupled to the lead frame.

Referring to FIG. 3, an implementation of a lead frame 34 isillustrated. The lead frame may be formed through stamping of the leadsto offset contacts with a first substrate and a second substrate. Afirst substrate 40 is coupled to a first side of the lead frame 34through leads 36 and wire bonds 38. In various implementations, the leadframe may be coupled to the first substrate through other electricallyconductive materials such as solders or die attach materials. The firstsubstrate includes two clips 42 and 44 coupled to a first side of thefirst substrate through electrically conductive bonding material. Invarious implementations, the electrically conductive bonding materialmay include, by non-limiting example, lead (Pb) free solder paste,silver sintering paste, other electrically conductive bonding materials,or any combination thereof. The two spacers 42 and 44 may be formed ofan electrically conductive material(s) and may provide electricalcontact between the first substrate and the second substrate. In variousimplementations, the spacers may be formed of copper or a copper alloy.

As illustrated in FIG. 3, a first side of a second substrate 46 iscoupled to the device through leads on the lead frame and through thetwo spacers 42 and 44 as illustrated by the dotted lines 48 and 50. Thesecond substrate includes two semiconductor die 52 and 54 coupled to afirst side of the substrate through electrically conductive material. Invarious implementations, the two die may include IGBTs, FRDs, or anyother die described herein. A clip 56 is coupled to a first side of eachof the two die. In various implementations, the clip may have athickness of about 0.3 mm. In other implementations, the thickness ofthe clip may be different based on electrical needs, thermal needs, orother design parameters of the device. In various implementations, theclips may be formed of copper or a copper alloy.

Referring to FIG. 4, an implementation of a first substrate 60 isillustrated. In various implementations, the first substrate may includea direct bonded copper substrate. In various implementations, thethickness of the layers of the substrate may be about 0.30 mm Cu, about0.32 mm ceramic, and about 0.30 mm Cu. In some implementations, thethicknesses of the layers may be different based on theparameters/structure of the device. The first substrate 60 includes afirst die 62 coupled to a first side 65 of the substrate. A clip 64 iscoupled to a first side of the first die 62. In various implementations,the first die may be a FRD die. As illustrated, the first substrate 60also includes a second die 66 coupled to a first side 65 of the firstsubstrate 60. In some implementations, the second die may include anIGBT die. A clip 68 is coupled to a first side of the second die 66through electrically conductive material. In various implementations,the clips may be formed from copper, a copper alloy, or anotherelectrically conductive material.

Referring to FIG. 5, an implementation of a second substrate 70 isillustrated. In various implementations, the second substrate mayinclude a direct bonded copper (DBC) substrate. In some implementations,the DBC may include an alumina (Al₂O₃) ceramic doped with zirconiumdioxide (ZrO₂) or any other combination described herein. The secondsubstrate 70 includes a first die 72 coupled to a first side 74 of thesubstrate. In various implementations, the first die may be a FRD die.As illustrated, a clip 76 is coupled to a first side of the first die72. In various implementations, the clip may be formed of copper, acopper alloy, or any other materials described for the clip herein. Invarious implementations, the clip may have a thickness of about 0.3 mm.In other implementations, the thickness of the clip may be larger orsmaller depending on electrical and thermal needs of the device. Asillustrated, the second substrate 70 also includes a second die 78coupled to a first side 74 of the first substrate 70. In someimplementations, the second die may include an IGBT die. A clip 80 iscoupled to a first side of the second die 78 through electricallyconductive material. In various implementations, the electricallyconductive material coupling the clips to the die may be hightemperature solder or high temperature sintering paste. The solder andthe sintering paste may include any die bonding or electrically couplingmaterial types described herein. When comparing FIG. 4, the firstsubstrate 60, with FIG. 5, the second substrate 70, it should be notedthat the clips have different orientations on each substrate. Thisdifference in orientation may help to offset the substrates when coupledto the lead frame.

Semiconductor packages as described herein may be manufactured throughvarious implementations of a method of forming semiconductor packages.The method may include providing a panel of first substrates. The methodmay include module sub assembly (MSA) in panel form including two setsof panels, a first panel of first substrates and a second panel ofsecond substrates. Referring to FIG. 6, a panel 82 of a plurality offirst substrates 84 is illustrated. The method may also includeproviding a panel of a plurality of second substrates. For ease ofillustration, only a panel of first substrates is illustrated though themethod of preparing the panel of second substrates is similar. Referringagain to FIGS. 4 and 5, the first substrates 60 and the secondsubstrates 70 do have slightly different orientations and positions inthe coupling of the clips and the coupling of electrically conductivematerial to the first side of each substrate. Each of the firstsubstrates and the second substrates may include DBC substrates. Invarious implementations, the initial thickness of each of the layers ofa substrate may include about 0.30 mm Cu, about 0.32 mm ceramic, andabout 0.30 mm Cu. In some implementations, the ceramic layer may includean Al₂O₃ ceramic doped with ZrO₂. In other implementations, the ceramiclayer may include a silicon nitride (Si3N4) ceramic, an aluminum nitride(AlN) ceramic, a high strength AlN (H—AlN) ceramic, or any combinationthereof. In still other implementations, the first substrate and thesecond substrate may include an insulated metal substrate technology(IMST), an active metal brazed (AMB) substrate, or any other substratementioned herein.

The method may also include printing a first electrically conductivebonding material on the first side of each of the first panel ofsubstrates and the second panel of substrates in predeterminedlocations. In various implementations, the electrically conductivematerial may include a high temperature solder or a high temperaturesintering paste. In some implementations, the solder may be a lead freesolder such as SnAg_(3.5) including 96.5% tin (Sn) and 3.5% silver (Ag)or SAC305 including 96.5 Sn, 3% Ag, and 0.5% copper (Cu). In otherimplementations, the electrically conductive bonding material mayinclude a silver sintering paste. Referring to FIG. 7, a first panel ofsubstrates 82 is illustrated after coupling of the electricallyconductive material 85 in the predetermined locations 86 to each of theplurality of first substrates 88.

The method may also include coupling two or more die to each of thefirst panel of substrates and the second panel of substrates. The two ormore die may be coupled to the substrates in the predetermined locationsof the electrically conductive bonding material. In variousimplementations, the die may include IGBTs, FRDs, or any othersemiconductor die described herein. Referring to FIG. 8, a panel 82 ofsubstrates 84 is illustrated after coupling two die 90 and 92 to each ofthe two predetermined locations 86 and 88. The method may also includedispensing a second electrically conductive material onto a second sideor exposed surface of the each of the two or more die. In variousimplementations, the second electrically conductive material may be thesame material printed onto a first side of the substrate or any otherelectrically conductive material disclosed in this document. Referringto FIG. 9, the panel 82 of substrates 84 is illustrated after dispensingthe second electrically conductive material 94 onto the second side ofeach of the two die 90 and 92.

The method may further include coupling a clip to each of the two ormore die through the second electrically conductive material. In someimplementations, the clips may be coupled to the die through pressuredsintering. Referring to FIG. 10, the panel 82 of substrates 84 isillustrated after the clips 96 and 98 have been coupled to the die 90and 92 through the electrically conductive material. Variousimplementations of this method may allow for uniform pressure to beapplied to the substrates since clips are mounted prior to assembly in asemiconductor package. As illustrated, the clips are placedperpendicularly to the leads of the lead frame. Referring to FIG. 11, animplementation of a clip is illustrated. In various implementations, theclips may have a thickness of about 0.3 mm, though in otherimplementations, the thickness of the clips may be larger or smallerbased on the electrical or thermal needs of the device. The clips may beflexible in various implementations for similar sized die, which mayreduce stress on the die. In some implementations, the clips may beformed from copper or a copper alloy.

The method may further include reflowing the solder or sintering pasteand flux cleaning of the surface of the substrates. The method may theninclude electrically coupling the two or more die to each of theplurality of first substrates and the plurality of second substrates. Asillustrated in FIG. 12, the die 90 may be coupled to the substrates 88through wire bonds 102. In various implementations, the wire bonds maybe formed of aluminum or other electrically conductive material. Whilethe use of wirebonds is illustrated in FIG. 12, in otherimplementations, other electrical connectors may be used to connect theclips, such as, by non-limiting example, bumps, stud bumps, pillars, orany other electrical connector type.

The method may also include singulating the first panel of substratesand the second panel of substrates each into a plurality of firstsubstrates and second substrates. In various implementations, the panelsof substrates may have scoring lines between each of the plurality ofsubstrates (or may be first scored to form such lines using a stylus)and the substrates may be singulated through breaking on the scoredlines. In other implementations, the plurality of substrates may besingulated through laser cutting. In still other implementations, thepanels may be singulated into a plurality of substrates through sawing.Referring to FIG. 13, the panel 82 is illustrated after some of theplurality of substrates 84 have been singulated from the panel. Invarious implementations, each of the substrates may be probe testedprior to singulation or after singulation and before coupling thesubstrates to the lead frames.

The method may also include dispensing solder onto a plurality ofpredetermined locations on the first side of each of the firstsubstrates and the second substrates. In various implementations, thesolder may be a low temperature solder. Referring to FIGS. 14 and 15,each of a first substrate 104 and a second substrate 106 is illustratedafter dispensing solder in predetermined locations 108. The method mayalso include coupling a first substrate to a first side of a lead frame.The first side of the first substrate may be coupled to the lead framethrough solder at the predetermined locations. The leads coupling withthe first substrate may be formed towards the first side of the leadframe. Referring to FIG. 16, the lead frame is illustrated aftercoupling the first substrate 104 to the first side of the lead frame110.

The method may also include coupling two or more spacers to a first sideof the first substrate on the predetermined locations not coupled to thelead frame. The clips may be formed of electrically conductive material.The spacers may electrically couple the first substrate to the secondsubstrate. Because the first substrate and the second substrates arecoupled only through the spacers, there may be less stress on thecomponents of the semiconductor package during assembly, reflow, andother processing steps of manufacturing. Still referring to FIG. 16, thetwo spacers 112 are illustrated coupled to a first side of the firstsubstrate 104 through solder. An enlarged view of the spacer 112 isillustrated in FIG. 17. In various implementations, the spacers may beformed of electrically conductive material such as copper. The methodalso includes coupling a first side of a second substrate 106 to the twospacers and to the second side of the lead frame as illustrated by thedotted lines 114 in FIG. 16. The leads that couple with the secondsubstrate are formed towards the second side of the lead frame.

Referring to FIG. 18, an implementation of a semiconductor package 116after coupling of the first side of the second substrate 106 to the twospacers and to the second side of the lead frame 110 is illustrated. Asillustrated, the first side of the first substrate and first side of thesecond substrate are asymmetrically coupled through the two spacers.This structure may place less stress on the internal components of thepackage. Referring to FIG. 19, a first side of the lead frame 110 isillustrated. The second side 118 of the first substrate 104 and a firstside of the second substrate 106 is visible in this view. The secondside of each of the first substrate and the second substrate are exposedto act as a heatsink for the semiconductor package.

Referring to FIG. 20, a side view of a semiconductor package 120 isillustrated. In this view, the lead frame 122 is illustrated having thefirst substrate 124 coupled to a first side of the lead frame 122 andthe second substrate 126 coupled to the second side of the lead frame122. The first substrate 124 and the second substrate 126 aremechanically and electrically coupled to the lead frame 122 throughleads 128 formed towards the respective substrates. The first substrate124 has two die 130 and 132 coupled to the first side of the firstsubstrate 124. Clips 134 and 136 are coupled to each of the two dies 130and 132. The structure of the semiconductor package allows the clips tobe coupled perpendicularly with the leads of the lead frame.

The semiconductor package also include spacers 138 and 140 thatmechanically and electrically couple the first substrate 124 with thesecond substrate 126. The first side of the first substrate and firstside of the second substrate are asymmetrically coupled through the twoor more spacers. The second substrate 126 includes two die 142 and 144coupled with the first side of the second substrate 126. Two clips 146and 148 are coupled with the two die 142 and 144. Coupling the firstsubstrate and the second substrate through the spacers asymmetricallymay reduce stress on the clips and the die of the semiconductor package.Use of the lead frame and use of the spacers allows for a structurewhere the substrates and the die are not coupled in a stackedconfiguration.

The method of manufacturing a semiconductor package may also includeencapsulating the lead frame on the first side and the second side. Invarious implementations, the packages may be encapsulated throughtransfer molding using epoxy molding compounds or through liquidprocesses using liquid encapsulants. The molding compounds may include,in various implementations, epoxies, resins, or other encapsulatingmaterials. A second side of each of the first substrate and the secondsubstrate 106 is exposed after encapsulation 150 as illustrated in FIG.21. The structure of the semiconductor package 120 may also providebetter mold flow during the molding process. The method may also includetrimming and forming the leads 152 of the semiconductor package 120 toorient them in desired direction(s) as illustrated in FIG. 22. Invarious implementations, the method may also include coupling a heatsink to the second side of the first substrate, the second side of thesecond substrate, the second side of the first die, the second side ofthe second die, or any combination thereof.

In places where the description above refers to particularimplementations of semiconductor packages and implementing components,sub-components, methods and sub-methods, it should be readily apparentthat a number of modifications may be made without departing from thespirit thereof and that these implementations, implementing components,sub-components, methods and sub-methods may be applied to othersemiconductor packages.

What is claimed is:
 1. A semiconductor package comprising: a firstsubstrate comprising two or more die coupled to a first side of thefirst substrate, wherein a clip is coupled to each of the two or moredie; a second substrate comprising two or more die coupled to a firstside of the second substrate, wherein a clip is coupled to each of thetwo or more die; two or more spacers coupled to the first side of thefirst substrate; and a lead frame comprised between the first substrateand the second substrate; a molding compound encapsulating the leadframe wherein a second side of each of the first substrate and thesecond substrate are exposed through the molding compound; and wherein aperimeter of the first substrate and a perimeter of the second substratedo not fully overlap when coupled through the two or more spacers. 2.The semiconductor package of claim 1, wherein the two or more dieinclude an insulated-gate bipolar transistors (IGBT) and a fast recoverydie (FRD).
 3. The semiconductor package of claim 1, wherein the firstsubstrate and the second substrate comprise a direct bonded coppersubstrate with one of an alumina (Al₂O₃) ceramic doped with zirconiumdioxide (ZrO₂), a silicon nitride (Si3N4) ceramic, an aluminum nitride(AlN) ceramic, a high strength AlN (H—AlN) ceramic, and any combinationthereof.
 4. The semiconductor package of claim 1, further comprising aheat sink coupled with one of the second side of the first substrate,the second side of the second substrate, or any combination thereof. 5.The semiconductor package of claim 1, wherein the two or more spacersare comprised of electrically conductive material and electricallycouple the first substrate to the second substrate.
 6. The semiconductorpackage of claim 1, wherein the first substrate and the second substratecomprise one of a direct bonded copper substrate (DBC), an insulatedmetal substrate technology (IMST) substrate, an active metal bonding(AMB) substrate, or any combination thereof.
 7. A semiconductor packagecomprising: a lead frame; a first substrate mechanically andelectrically coupled to a first side of the lead frame, the firstsubstrate comprising two or more die on the first side of the firstsubstrate, wherein a clip is coupled to each of the two or more die; asecond substrate mechanically and electrically coupled to a second sideof the lead frame, the second substrate comprising two or more die onthe first side of the second substrate, wherein a clip is coupled toeach of the two or more die; two or more spacers coupled to the firstside of each of the first substrate and the second substrate; and amolding compound encapsulating the first side and the second side of thelead frame; wherein the first side of the first substrate and first sideof the second substrate are asymmetrically coupled through the two ormore spacers.
 8. The semiconductor package of claim 7, wherein the twoor more die include an insulated-gate bipolar transistors (IGBT) and afast recovery die (FRD).
 9. The semiconductor package of claim 7,wherein the first substrate and the second substrate comprise a directbonded copper substrate with one of an alumina (Al₂O₃) ceramic dopedwith zirconium dioxide (ZrO₂), a silicon nitride (Si3N4) ceramic, analuminum nitride (AlN) ceramic, a high strength AlN (H—AlN) ceramic, andany combination thereof.
 10. The semiconductor package of claim 7,further comprising a heat sink coupled with one of the second side ofthe first substrate, the second side of the second substrate, or anycombination thereof.
 11. The semiconductor package of claim 7, whereinthe two or more spacers are comprised of electrically conductivematerial and electrically couple the first substrate to the secondsubstrate.
 12. The semiconductor package of claim 7, wherein the firstsubstrate and the second substrate comprise one of a direct bondedcopper substrate (DBC), an insulated metal substrate technology (IMST)substrate, an active metal bonding (AMB) substrate, or any combinationthereof.
 13. A method of forming semiconductor packages, the methodcomprising: providing a first panel of first substrates and a secondpanel of second substrates; printing a first electrically conductivebonding material on the first side of the first panel of substrates andthe second side of the first panel of first substrates in predeterminedlocations; coupling two or more die to each substrate of the first panelof first substrates and to each substrate of the second panel of secondsubstrates at the predetermined locations; dispensing a secondelectrically conductive material onto a second side of each of the twoor more die; coupling a clip to each of the two or more die;electrically coupling the two or more die to each substrate of the firstpanel of first substrates and to each substrate of the second panel ofsecond substrates; singulating each of the first panel and the secondpanel into a plurality of first substrates and a plurality of secondsubstrates, respectively; dispensing solder onto a plurality ofpredetermined locations on the first side of each of the plurality offirst substrates and each of the plurality of second substrates;coupling a first substrate of the plurality of first substrates to afirst side of a lead frame; coupling two or more spacers to a first sideof the first substrate; and coupling a first side of a second substrateof the plurality of second substrates to the two or more spacers and tothe second side of the lead frame.
 14. The method of claim 13, furthercomprising trimming the lead frame to expose a plurality of leads andforming the leads.
 15. The method of claim 13, further comprisingencapsulating the lead frame on the first side and the second side,wherein a second side of each substrate of the plurality of firstsubstrates and the plurality of second substrates is exposed.
 16. Themethod of claim 13, wherein the first panel of first substrates and thesecond panel of second substrates each comprise one of a direct bondedcopper substrate (DBC), an insulated metal substrate technology (IMST)substrate, an active metal bonding (AMB) substrate, or any combinationthereof.
 17. The method of claim 13, further comprising coupling a heatsink with one of the second side of the first substrate of the pluralityof first substrates, the second side of the second substrate of theplurality of second substrates, or any combination thereof.
 18. Themethod of claim 13, wherein the two or more spacers are comprised ofelectrically conductive material and electrically couple the firstsubstrate to the second substrate.
 19. The method of claim 13, whereinthe first side of the first substrate and first side of the secondsubstrate are asymmetrically coupled through the two or more spacers.20. The method of claim 13, wherein the first and the secondelectrically conductive material comprises one of a solder paste or asintering paste.